性能 Properey

GGD-1

GGD-2

GGD-3

GGD-4

GGD-5

牌號 Brand

化學成分（%）Chemical composition

SiO2≥

95

96

96

97

90

Al2O3≤

0.7

0.6

0.6

0.5

0.4

Fe2O3≤

0.5

0.5

0.4

0.4

0.8

冷態(tài)耐壓強度（Mpa)
Cold crushing strength

1350℃×3h
After firing at

15

15

10

10

25

顯氣孔率（％）
Ａpparent porosity 

1350℃×3h
After firing at

26

26

25

25

23

燒后線變化率（％）Linear changing after burnt

1350℃×3h
After firing at

0～+1.6

0～+1.6

0～+1.2

0～+1.2

0～+1.0

體積密度（g/cm3）Bulk density 

1350℃×3h
After firing at

2.0

2.0

2.1

2.1

2.2

耐火度(℃)
Refractoriness

1630

1650

1650

1680

—

大集料粒度(mm)Max. 
grain size of aggregate

5

4.5

4.5

4.2

4.2

施工用量(kg/m3)
Amount for construction

2300

2300

2300

2400

2400

施工方式
Mathod of construction

振動或搗打　Jolt or ramming

應(yīng)用  
Application

  青銅bronze

紫銅.黃銅copper  brass

白銅cupronickel  

鋼.鐵stee l  

 鋁及合金aluminium 

金屬熔煉爐、保溫爐　
Melting furance for nonferrous metals

特點
 Characteristic

價廉  保溫  節(jié)電  不沾渣  快速干燥  化學結(jié)合  耐侵蝕Cost down Thernalinsulation Economy 
electricity Nostickresidue Fast drying Chemicalbonded Corrosion resistance